CN3M (UNS J94652) chemical composition
Low-carbon, high-nickel fully austenitic grade of the 904L type (UNS J94652). The higher Ni and Mo levels give resistance to chloride stress-corrosion cracking and to reducing acids such as dilute sulphuric and phosphoric acid.
- Designation
- CN3M
- Material no.
- UNS J94652
- Standard
- ASTM A743
- Also known as
- ≈ 904L type (cast)
- Family
- Stainless cast steel
Chemical composition (mass %)
| Element | min | max |
|---|---|---|
| CCarbon | – | 0.03 |
| SiSilicon | – | 1.00 |
| MnManganese | – | 2.00 |
| PPhosphorus | – | 0.03 |
| SSulphur | – | 0.03 |
| CrChromium | 20.0 | 22.0 |
| NiNickel | 23.0 | 27.0 |
| MoMolybdenum | 4.50 | 5.50 |
| FeIron | remainder | |
Basis of values: Limits per ASTM A743.
We cast CN3M
Tsitouras Foundry supplies stainless steel sand castings – and centrifugal castings for bushings and sleeves – with the heat treatment each grade requires (solution annealing; quenching and tempering for martensitic grades), spectrometric chemical analysis, mechanical testing and NDT, EN 10204 3.1 certificates, and CNC machining to the finished part in the group's own machine shop.
- Sand casting at our foundry in Mandra, Attica; centrifugal casting for bushings, sleeves and liners
- Heat treatment at the foundry (water, oil or air quench); CNC machining in our machine shop in Perama
- Spectrometer analysis of every heat, mechanical testing and NDT
- EN 10204 3.1 inspection certificates; ISO 9001 (both plants) and ISO 14001 (foundry) certified
Other grades in this family
For information only, without warranty: limits per the cited standard or, where stated, typical or house values; ≈ marks a comparable grade, not an equivalent. The current edition of the standard, the purchase order and the drawing govern.