GX90MnMo14 (1.3417) chemical composition
Low-carbon, higher-manganese grade with molybdenum, the only manganese steel in the standard that may be supplied as-cast, for thin sections at the low end of its carbon range. The low carbon and Mo limit grain-boundary carbides, giving high toughness for impact-loaded parts such as track components and thick-walled wear castings.
- Designation
- GX90MnMo14
- Material no.
- 1.3417
- Standard
- EN 10349 / ISO 13521
- Also known as
- ≈ ZG90Mn14Mo1 (GB/T 5680)
- Family
- Austenitic manganese steel (Hadfield)
Chemical composition (mass %)
| Element | min | max |
|---|---|---|
| CCarbon | 0.70 | 1.00 |
| SiSilicon | 0.30 | 0.60 |
| MnManganese | 13.0 | 15.0 |
| PPhosphorus | – | 0.07 |
| SSulphur | – | 0.045 |
| MoMolybdenum | 1.00 | 1.80 |
| FeIron | remainder | |
Basis of values: Limits per EN 10349 / ISO 13521.
Additional requirements: May be supplied without heat treatment when wall thickness < 45 mm and C < 0.8 %; at ≥ 45 mm wall and C ≥ 0.8 % it shall be solution treated at not below 1040 °C and water-quenched
We cast GX90MnMo14
We sand-cast manganese steel wear parts at our foundry in Mandra and solution-anneal and water-quench them in-house. Chemistry is checked on every heat by spectrometer, mechanical tests are carried out, and parts are supplied with EN 10204 3.1 inspection certificates. Machining, where required, is done in the group's own CNC machine shop.
- Sand casting at our foundry in Mandra, Attica; centrifugal casting for bushings, sleeves and liners
- Heat treatment at the foundry (water, oil or air quench); CNC machining in our machine shop in Perama
- Spectrometer analysis of every heat, mechanical testing and NDT
- EN 10204 3.1 inspection certificates; ISO 9001 (both plants) and ISO 14001 (foundry) certified
Other grades in this family
For information only, without warranty: limits per the cited standard or, where stated, typical or house values; ≈ marks a comparable grade, not an equivalent. The current edition of the standard, the purchase order and the drawing govern.