GX120MnCr13-2 (1.3410) chemical composition
Chromium-alloyed version of the base grade: higher yield strength and initial hardness give better resistance to abrasion and deformation, at somewhat lower toughness. Used where abrasion matters as much as impact, e.g. jaws, blow bars and liners.
- Designation
- GX120MnCr13-2
- Material no.
- 1.3410
- Standard
- EN 10349 / ISO 13521
- Also known as
- GX120MnCr12-2, G-X120MnCr12-2, ≈ ASTM A128 Gr. C
- Family
- Austenitic manganese steel (Hadfield)
Chemical composition (mass %)
| Element | min | max |
|---|---|---|
| CCarbon | 1.05 | 1.35 |
| SiSilicon | 0.30 | 0.90 |
| MnManganese | 11.0 | 14.0 |
| PPhosphorus | – | 0.06 |
| SSulphur | – | 0.045 |
| CrChromium | 1.50 | 2.50 |
| FeIron | remainder | |
Basis of values: Limits per EN 10349 / ISO 13521.
We cast GX120MnCr13-2
We sand-cast manganese steel wear parts at our foundry in Mandra and solution-anneal and water-quench them in-house. Chemistry is checked on every heat by spectrometer, mechanical tests are carried out, and parts are supplied with EN 10204 3.1 inspection certificates. Machining, where required, is done in the group's own CNC machine shop.
- Sand casting at our foundry in Mandra, Attica; centrifugal casting for bushings, sleeves and liners
- Heat treatment at the foundry (water, oil or air quench); CNC machining in our machine shop in Perama
- Spectrometer analysis of every heat, mechanical testing and NDT
- EN 10204 3.1 inspection certificates; ISO 9001 (both plants) and ISO 14001 (foundry) certified
Other grades in this family
For information only, without warranty: limits per the cited standard or, where stated, typical or house values; ≈ marks a comparable grade, not an equivalent. The current edition of the standard, the purchase order and the drawing govern.